EN 1.4729 Stainless Steel vs. ASTM A387 Grade 5 Steel

Both EN 1.4729 stainless steel and ASTM A387 grade 5 steel are iron alloys. They have 90% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is EN 1.4729 stainless steel and the bottom bar is ASTM A387 grade 5 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 260
150 to 180
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 15
20 to 21
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 75
74

Thermal Properties

Latent Heat of Fusion, J/g 300
260
Maximum Temperature: Mechanical, °C 850
510
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 490
470
Thermal Conductivity, W/m-K 24
40
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.8
8.0
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
9.2

Otherwise Unclassified Properties

Base Metal Price, % relative 7.5
4.3
Density, g/cm3 7.6
7.8
Embodied Carbon, kg CO2/kg material 2.1
1.7
Embodied Energy, MJ/kg 29
23
Embodied Water, L/kg 100
69

Common Calculations

PREN (Pitting Resistance) 14
6.8
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Thermal Diffusivity, mm2/s 6.5
11

Alloy Composition

Carbon (C), % 0.3 to 0.5
0 to 0.15
Chromium (Cr), % 12 to 14
4.0 to 6.0
Iron (Fe), % 80.4 to 86.7
92.1 to 95.3
Manganese (Mn), % 0 to 1.0
0.3 to 0.6
Molybdenum (Mo), % 0 to 0.5
0.45 to 0.65
Nickel (Ni), % 0 to 1.0
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 1.0 to 2.5
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.025