EN 1.4729 Stainless Steel vs. SAE-AISI S2 Steel

Both EN 1.4729 stainless steel and SAE-AISI S2 steel are iron alloys. They have 86% of their average alloy composition in common. There are 19 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.4729 stainless steel and the bottom bar is SAE-AISI S2 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 75
72

Thermal Properties

Latent Heat of Fusion, J/g 300
260
Melting Completion (Liquidus), °C 1420
1450
Melting Onset (Solidus), °C 1380
1410
Specific Heat Capacity, J/kg-K 490
470
Thermal Conductivity, W/m-K 24
44
Thermal Expansion, µm/m-K 10
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.8
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 7.5
2.6
Density, g/cm3 7.6
7.8
Embodied Carbon, kg CO2/kg material 2.1
2.1
Embodied Energy, MJ/kg 29
30
Embodied Water, L/kg 100
49

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Thermal Diffusivity, mm2/s 6.5
12

Alloy Composition

Carbon (C), % 0.3 to 0.5
0.4 to 0.55
Chromium (Cr), % 12 to 14
0
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 80.4 to 86.7
96 to 98.1
Manganese (Mn), % 0 to 1.0
0.3 to 0.5
Molybdenum (Mo), % 0 to 0.5
0.3 to 0.6
Nickel (Ni), % 0 to 1.0
0 to 0.3
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 1.0 to 2.5
0.9 to 1.2
Sulfur (S), % 0 to 0.030
0 to 0.030
Vanadium (V), % 0
0 to 0.5