EN 1.4729 Stainless Steel vs. K93603 Alloy

Both EN 1.4729 stainless steel and K93603 alloy are iron alloys. They have 64% of their average alloy composition in common. There are 15 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is EN 1.4729 stainless steel and the bottom bar is K93603 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.28
0.3
Shear Modulus, GPa 75
72

Thermal Properties

Latent Heat of Fusion, J/g 300
270
Melting Completion (Liquidus), °C 1420
1430
Melting Onset (Solidus), °C 1380
1380
Specific Heat Capacity, J/kg-K 490
460
Thermal Expansion, µm/m-K 10
12

Otherwise Unclassified Properties

Base Metal Price, % relative 7.5
25
Density, g/cm3 7.6
8.2
Embodied Carbon, kg CO2/kg material 2.1
4.8
Embodied Energy, MJ/kg 29
66
Embodied Water, L/kg 100
120

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
23

Alloy Composition

Aluminum (Al), % 0
0 to 0.1
Carbon (C), % 0.3 to 0.5
0 to 0.050
Chromium (Cr), % 12 to 14
0 to 0.25
Cobalt (Co), % 0
0 to 0.5
Iron (Fe), % 80.4 to 86.7
61.8 to 64
Magnesium (Mg), % 0
0 to 0.1
Manganese (Mn), % 0 to 1.0
0 to 0.6
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 0 to 1.0
36
Phosphorus (P), % 0 to 0.040
0 to 0.015
Silicon (Si), % 1.0 to 2.5
0 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.015
Titanium (Ti), % 0
0 to 0.1
Zirconium (Zr), % 0
0 to 0.1