EN 1.4742 Stainless Steel vs. Z41121 Zinc

EN 1.4742 stainless steel belongs to the iron alloys classification, while Z41121 zinc belongs to the zinc alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4742 stainless steel and the bottom bar is Z41121 zinc.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
87
Elongation at Break, % 17
50
Poisson's Ratio 0.28
0.25
Shear Modulus, GPa 77
35
Tensile Strength: Ultimate (UTS), MPa 600
140
Tensile Strength: Yield (Proof), MPa 300
120

Thermal Properties

Latent Heat of Fusion, J/g 290
110
Maximum Temperature: Mechanical, °C 1000
90
Melting Completion (Liquidus), °C 1420
410
Melting Onset (Solidus), °C 1380
400
Specific Heat Capacity, J/kg-K 490
390
Thermal Conductivity, W/m-K 19
110
Thermal Expansion, µm/m-K 11
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.9
27
Electrical Conductivity: Equal Weight (Specific), % IACS 2.2
37

Otherwise Unclassified Properties

Base Metal Price, % relative 9.0
11
Density, g/cm3 7.6
6.6
Embodied Carbon, kg CO2/kg material 2.2
2.8
Embodied Energy, MJ/kg 32
54
Embodied Water, L/kg 130
340

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 84
68
Resilience: Unit (Modulus of Resilience), kJ/m3 230
79
Stiffness to Weight: Axial, points 14
7.4
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 22
6.1
Strength to Weight: Bending, points 21
9.3
Thermal Diffusivity, mm2/s 5.1
44
Thermal Shock Resistance, points 21
4.6

Alloy Composition

Aluminum (Al), % 0.7 to 1.2
0 to 0.010
Cadmium (Cd), % 0
0 to 0.0050
Carbon (C), % 0 to 0.12
0
Chromium (Cr), % 17 to 19
0
Copper (Cu), % 0
0.080 to 0.49
Iron (Fe), % 77.2 to 81.6
0 to 0.010
Lead (Pb), % 0
0 to 0.010
Manganese (Mn), % 0 to 1.0
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0.7 to 1.4
0
Sulfur (S), % 0 to 0.015
0
Tin (Sn), % 0
0 to 0.0030
Titanium (Ti), % 0
0.050 to 0.18
Zinc (Zn), % 0
99.292 to 99.87