EN 1.4806 Stainless Steel vs. ASTM A182 Grade F24

Both EN 1.4806 stainless steel and ASTM A182 grade F24 are iron alloys. They have 48% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4806 stainless steel and the bottom bar is ASTM A182 grade F24.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
210
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 6.8
23
Fatigue Strength, MPa 120
330
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 75
74
Tensile Strength: Ultimate (UTS), MPa 470
670
Tensile Strength: Yield (Proof), MPa 250
460

Thermal Properties

Latent Heat of Fusion, J/g 320
260
Maximum Temperature: Mechanical, °C 1000
460
Melting Completion (Liquidus), °C 1380
1470
Melting Onset (Solidus), °C 1340
1430
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 12
39
Thermal Expansion, µm/m-K 15
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.8

Otherwise Unclassified Properties

Base Metal Price, % relative 31
4.0
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 5.4
2.3
Embodied Energy, MJ/kg 76
33
Embodied Water, L/kg 190
61

Common Calculations

PREN (Pitting Resistance) 18
6.7
Resilience: Ultimate (Unit Rupture Work), MJ/m3 27
140
Resilience: Unit (Modulus of Resilience), kJ/m3 160
570
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 16
24
Strength to Weight: Bending, points 17
22
Thermal Diffusivity, mm2/s 3.1
11
Thermal Shock Resistance, points 11
19

Alloy Composition

Aluminum (Al), % 0
0 to 0.020
Boron (B), % 0
0.0015 to 0.0070
Carbon (C), % 0.3 to 0.5
0.050 to 0.1
Chromium (Cr), % 16 to 18
2.2 to 2.6
Iron (Fe), % 40.4 to 48.7
94.5 to 96.1
Manganese (Mn), % 0 to 2.0
0.3 to 0.7
Molybdenum (Mo), % 0 to 0.5
0.9 to 1.1
Nickel (Ni), % 34 to 36
0
Nitrogen (N), % 0
0 to 0.12
Phosphorus (P), % 0 to 0.040
0 to 0.020
Silicon (Si), % 1.0 to 2.5
0.15 to 0.45
Sulfur (S), % 0 to 0.030
0 to 0.010
Titanium (Ti), % 0
0.060 to 0.1
Vanadium (V), % 0
0.2 to 0.3