EN 1.4806 Stainless Steel vs. EN 1.0258 Steel

Both EN 1.4806 stainless steel and EN 1.0258 steel are iron alloys. They have 46% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4806 stainless steel and the bottom bar is EN 1.0258 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
140
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 6.8
23
Fatigue Strength, MPa 120
200
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 75
73
Tensile Strength: Ultimate (UTS), MPa 470
490
Tensile Strength: Yield (Proof), MPa 250
290

Thermal Properties

Latent Heat of Fusion, J/g 320
250
Maximum Temperature: Mechanical, °C 1000
400
Melting Completion (Liquidus), °C 1380
1460
Melting Onset (Solidus), °C 1340
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 12
49
Thermal Expansion, µm/m-K 15
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 31
2.1
Density, g/cm3 8.0
7.9
Embodied Carbon, kg CO2/kg material 5.4
1.5
Embodied Energy, MJ/kg 76
19
Embodied Water, L/kg 190
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 27
95
Resilience: Unit (Modulus of Resilience), kJ/m3 160
220
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 16
17
Strength to Weight: Bending, points 17
18
Thermal Diffusivity, mm2/s 3.1
13
Thermal Shock Resistance, points 11
16

Alloy Composition

Carbon (C), % 0.3 to 0.5
0 to 0.2
Chromium (Cr), % 16 to 18
0 to 0.3
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 40.4 to 48.7
96.9 to 100
Manganese (Mn), % 0 to 2.0
0 to 1.4
Molybdenum (Mo), % 0 to 0.5
0 to 0.080
Nickel (Ni), % 34 to 36
0 to 0.3
Niobium (Nb), % 0
0 to 0.010
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 1.0 to 2.5
0 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.020
Titanium (Ti), % 0
0 to 0.040
Vanadium (V), % 0
0 to 0.020