MakeItFrom.com
Menu (ESC)

EN 1.4806 Stainless Steel vs. EN 1.4062 Stainless Steel

Both EN 1.4806 stainless steel and EN 1.4062 stainless steel are iron alloys. They have 65% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4806 stainless steel and the bottom bar is EN 1.4062 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 6.8
23 to 34
Fatigue Strength, MPa 120
410 to 420
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 75
79
Tensile Strength: Ultimate (UTS), MPa 470
770 to 800
Tensile Strength: Yield (Proof), MPa 250
530 to 600

Thermal Properties

Latent Heat of Fusion, J/g 320
290
Maximum Temperature: Corrosion, °C 400
440
Maximum Temperature: Mechanical, °C 1000
1030
Melting Completion (Liquidus), °C 1380
1430
Melting Onset (Solidus), °C 1340
1380
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 12
15
Thermal Expansion, µm/m-K 15
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 31
12
Density, g/cm3 8.0
7.7
Embodied Carbon, kg CO2/kg material 5.4
2.6
Embodied Energy, MJ/kg 76
37
Embodied Water, L/kg 190
150

Common Calculations

PREN (Pitting Resistance) 18
27
Resilience: Ultimate (Unit Rupture Work), MJ/m3 27
170 to 230
Resilience: Unit (Modulus of Resilience), kJ/m3 160
690 to 910
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 16
28 to 29
Strength to Weight: Bending, points 17
24 to 25
Thermal Diffusivity, mm2/s 3.1
4.0
Thermal Shock Resistance, points 11
21 to 22

Alloy Composition

Carbon (C), % 0.3 to 0.5
0 to 0.030
Chromium (Cr), % 16 to 18
21.5 to 24
Iron (Fe), % 40.4 to 48.7
69.3 to 77.3
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 0 to 0.5
0 to 0.45
Nickel (Ni), % 34 to 36
1.0 to 2.9
Nitrogen (N), % 0
0.16 to 0.28
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 1.0 to 2.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.010