EN 1.4806 Stainless Steel vs. EN 1.4405 Stainless Steel

Both EN 1.4806 stainless steel and EN 1.4405 stainless steel are iron alloys. They have 67% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4806 stainless steel and the bottom bar is EN 1.4405 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 6.8
17
Fatigue Strength, MPa 120
370
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 75
77
Tensile Strength: Ultimate (UTS), MPa 470
860
Tensile Strength: Yield (Proof), MPa 250
610

Thermal Properties

Latent Heat of Fusion, J/g 320
280
Maximum Temperature: Corrosion, °C 400
410
Maximum Temperature: Mechanical, °C 1000
870
Melting Completion (Liquidus), °C 1380
1450
Melting Onset (Solidus), °C 1340
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 12
17
Thermal Expansion, µm/m-K 15
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 31
13
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 5.4
2.8
Embodied Energy, MJ/kg 76
39
Embodied Water, L/kg 190
130

Common Calculations

PREN (Pitting Resistance) 18
20
Resilience: Ultimate (Unit Rupture Work), MJ/m3 27
130
Resilience: Unit (Modulus of Resilience), kJ/m3 160
950
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 16
31
Strength to Weight: Bending, points 17
26
Thermal Diffusivity, mm2/s 3.1
4.6
Thermal Shock Resistance, points 11
29

Alloy Composition

Carbon (C), % 0.3 to 0.5
0 to 0.060
Chromium (Cr), % 16 to 18
15 to 17
Iron (Fe), % 40.4 to 48.7
73.6 to 80.3
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 0 to 0.5
0.7 to 1.5
Nickel (Ni), % 34 to 36
4.0 to 6.0
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 1.0 to 2.5
0 to 0.8
Sulfur (S), % 0 to 0.030
0 to 0.025