EN 1.4806 Stainless Steel vs. EN 1.4835 Stainless Steel

Both EN 1.4806 stainless steel and EN 1.4835 stainless steel are iron alloys. They have 75% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4806 stainless steel and the bottom bar is EN 1.4835 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
180
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 6.8
43
Fatigue Strength, MPa 120
310
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 75
77
Tensile Strength: Ultimate (UTS), MPa 470
750
Tensile Strength: Yield (Proof), MPa 250
350

Thermal Properties

Latent Heat of Fusion, J/g 320
320
Maximum Temperature: Corrosion, °C 400
430
Maximum Temperature: Mechanical, °C 1000
1150
Melting Completion (Liquidus), °C 1380
1400
Melting Onset (Solidus), °C 1340
1360
Specific Heat Capacity, J/kg-K 480
490
Thermal Conductivity, W/m-K 12
15
Thermal Expansion, µm/m-K 15
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 31
17
Density, g/cm3 8.0
7.7
Embodied Carbon, kg CO2/kg material 5.4
3.3
Embodied Energy, MJ/kg 76
47
Embodied Water, L/kg 190
160

Common Calculations

PREN (Pitting Resistance) 18
24
Resilience: Ultimate (Unit Rupture Work), MJ/m3 27
270
Resilience: Unit (Modulus of Resilience), kJ/m3 160
310
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 16
27
Strength to Weight: Bending, points 17
24
Thermal Diffusivity, mm2/s 3.1
4.0
Thermal Shock Resistance, points 11
16

Alloy Composition

Carbon (C), % 0.3 to 0.5
0.050 to 0.12
Cerium (Ce), % 0
0.030 to 0.080
Chromium (Cr), % 16 to 18
20 to 22
Iron (Fe), % 40.4 to 48.7
62 to 68.4
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 34 to 36
10 to 12
Nitrogen (N), % 0
0.12 to 0.2
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 1.0 to 2.5
1.4 to 2.5
Sulfur (S), % 0 to 0.030
0 to 0.015