EN 1.4806 Stainless Steel vs. EN 1.6522 Steel

Both EN 1.4806 stainless steel and EN 1.6522 steel are iron alloys. They have 47% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.4806 stainless steel and the bottom bar is EN 1.6522 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
150 to 190
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 75
73
Tensile Strength: Ultimate (UTS), MPa 470
500 to 1460

Thermal Properties

Latent Heat of Fusion, J/g 320
250
Maximum Temperature: Mechanical, °C 1000
410
Melting Completion (Liquidus), °C 1380
1460
Melting Onset (Solidus), °C 1340
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 12
39
Thermal Expansion, µm/m-K 15
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 31
2.6
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 5.4
1.5
Embodied Energy, MJ/kg 76
20
Embodied Water, L/kg 190
51

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 16
18 to 52
Strength to Weight: Bending, points 17
18 to 36
Thermal Diffusivity, mm2/s 3.1
10
Thermal Shock Resistance, points 11
15 to 43

Alloy Composition

Aluminum (Al), % 0
0 to 0.050
Carbon (C), % 0.3 to 0.5
0.17 to 0.23
Chromium (Cr), % 16 to 18
0.35 to 0.7
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 40.4 to 48.7
96.6 to 98.5
Manganese (Mn), % 0 to 2.0
0.6 to 1.0
Molybdenum (Mo), % 0 to 0.5
0.15 to 0.25
Nickel (Ni), % 34 to 36
0.4 to 0.7
Oxygen (O), % 0
0 to 0.0020
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 1.0 to 2.5
0 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.030