EN 1.4806 Stainless Steel vs. EN 1.7108 Steel

Both EN 1.4806 stainless steel and EN 1.7108 steel are iron alloys. They have 48% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.4806 stainless steel and the bottom bar is EN 1.7108 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
200 to 510
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 75
72
Tensile Strength: Ultimate (UTS), MPa 470
670 to 2070

Thermal Properties

Latent Heat of Fusion, J/g 320
280
Maximum Temperature: Mechanical, °C 1000
410
Melting Completion (Liquidus), °C 1380
1430
Melting Onset (Solidus), °C 1340
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 12
46
Thermal Expansion, µm/m-K 15
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 31
2.1
Density, g/cm3 8.0
7.7
Embodied Carbon, kg CO2/kg material 5.4
1.5
Embodied Energy, MJ/kg 76
20
Embodied Water, L/kg 190
47

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 16
24 to 75
Strength to Weight: Bending, points 17
22 to 47
Thermal Diffusivity, mm2/s 3.1
12
Thermal Shock Resistance, points 11
20 to 63

Alloy Composition

Carbon (C), % 0.3 to 0.5
0.57 to 0.65
Chromium (Cr), % 16 to 18
0.2 to 0.45
Iron (Fe), % 40.4 to 48.7
95.9 to 96.9
Manganese (Mn), % 0 to 2.0
0.7 to 1.0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 34 to 36
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 1.0 to 2.5
1.6 to 2.0
Sulfur (S), % 0 to 0.030
0 to 0.025