EN 1.4806 Stainless Steel vs. SAE-AISI 5147 Steel

Both EN 1.4806 stainless steel and SAE-AISI 5147 steel are iron alloys. They have 47% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4806 stainless steel and the bottom bar is SAE-AISI 5147 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
180
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 6.8
20
Fatigue Strength, MPa 120
250
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 75
73
Tensile Strength: Ultimate (UTS), MPa 470
600
Tensile Strength: Yield (Proof), MPa 250
360

Thermal Properties

Latent Heat of Fusion, J/g 320
250
Maximum Temperature: Mechanical, °C 1000
420
Melting Completion (Liquidus), °C 1380
1450
Melting Onset (Solidus), °C 1340
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 12
46
Thermal Expansion, µm/m-K 15
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 31
2.2
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 5.4
1.5
Embodied Energy, MJ/kg 76
19
Embodied Water, L/kg 190
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 27
110
Resilience: Unit (Modulus of Resilience), kJ/m3 160
360
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 16
21
Strength to Weight: Bending, points 17
20
Thermal Diffusivity, mm2/s 3.1
12
Thermal Shock Resistance, points 11
18

Alloy Composition

Carbon (C), % 0.3 to 0.5
0.46 to 0.51
Chromium (Cr), % 16 to 18
0.85 to 1.2
Iron (Fe), % 40.4 to 48.7
97 to 97.8
Manganese (Mn), % 0 to 2.0
0.7 to 1.0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 34 to 36
0
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 1.0 to 2.5
0.15 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.040