EN 1.4806 Stainless Steel vs. N08367 Stainless Steel

Both EN 1.4806 stainless steel and N08367 stainless steel are iron alloys. They have 88% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4806 stainless steel and the bottom bar is N08367 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
210
Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 6.8
34
Fatigue Strength, MPa 120
280
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 75
80
Tensile Strength: Ultimate (UTS), MPa 470
740
Tensile Strength: Yield (Proof), MPa 250
350

Thermal Properties

Latent Heat of Fusion, J/g 320
310
Maximum Temperature: Corrosion, °C 400
430
Maximum Temperature: Mechanical, °C 1000
1100
Melting Completion (Liquidus), °C 1380
1460
Melting Onset (Solidus), °C 1340
1410
Specific Heat Capacity, J/kg-K 480
460
Thermal Conductivity, W/m-K 12
12
Thermal Expansion, µm/m-K 15
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
1.8
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
2.0

Otherwise Unclassified Properties

Base Metal Price, % relative 31
33
Density, g/cm3 8.0
8.1
Embodied Carbon, kg CO2/kg material 5.4
6.2
Embodied Energy, MJ/kg 76
84
Embodied Water, L/kg 190
200

Common Calculations

PREN (Pitting Resistance) 18
46
Resilience: Ultimate (Unit Rupture Work), MJ/m3 27
210
Resilience: Unit (Modulus of Resilience), kJ/m3 160
290
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 16
25
Strength to Weight: Bending, points 17
22
Thermal Diffusivity, mm2/s 3.1
3.2
Thermal Shock Resistance, points 11
17

Alloy Composition

Carbon (C), % 0.3 to 0.5
0 to 0.030
Chromium (Cr), % 16 to 18
20 to 22
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 40.4 to 48.7
41.4 to 50.3
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 0 to 0.5
6.0 to 7.0
Nickel (Ni), % 34 to 36
23.5 to 25.5
Nitrogen (N), % 0
0.18 to 0.25
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 1.0 to 2.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030