EN 1.4806 Stainless Steel vs. S30435 Stainless Steel

Both EN 1.4806 stainless steel and S30435 stainless steel are iron alloys. They have 71% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4806 stainless steel and the bottom bar is S30435 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
160
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 6.8
51
Fatigue Strength, MPa 120
170
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 75
76
Tensile Strength: Ultimate (UTS), MPa 470
510
Tensile Strength: Yield (Proof), MPa 250
170

Thermal Properties

Latent Heat of Fusion, J/g 320
280
Maximum Temperature: Corrosion, °C 400
410
Maximum Temperature: Mechanical, °C 1000
900
Melting Completion (Liquidus), °C 1380
1420
Melting Onset (Solidus), °C 1340
1380
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 12
16
Thermal Expansion, µm/m-K 15
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
2.8

Otherwise Unclassified Properties

Base Metal Price, % relative 31
14
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 5.4
2.9
Embodied Energy, MJ/kg 76
40
Embodied Water, L/kg 190
140

Common Calculations

PREN (Pitting Resistance) 18
17
Resilience: Ultimate (Unit Rupture Work), MJ/m3 27
210
Resilience: Unit (Modulus of Resilience), kJ/m3 160
77
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 16
18
Strength to Weight: Bending, points 17
18
Thermal Diffusivity, mm2/s 3.1
4.2
Thermal Shock Resistance, points 11
12

Alloy Composition

Carbon (C), % 0.3 to 0.5
0 to 0.080
Chromium (Cr), % 16 to 18
16 to 18
Copper (Cu), % 0
1.5 to 3.0
Iron (Fe), % 40.4 to 48.7
66.9 to 75.5
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 34 to 36
7.0 to 9.0
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 1.0 to 2.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030