EN 1.4806 Stainless Steel vs. S32760 Stainless Steel

Both EN 1.4806 stainless steel and S32760 stainless steel are iron alloys. They have 70% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4806 stainless steel and the bottom bar is S32760 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
250
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 6.8
28
Fatigue Strength, MPa 120
450
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 75
80
Tensile Strength: Ultimate (UTS), MPa 470
850
Tensile Strength: Yield (Proof), MPa 250
620

Thermal Properties

Latent Heat of Fusion, J/g 320
300
Maximum Temperature: Corrosion, °C 400
450
Maximum Temperature: Mechanical, °C 1000
1100
Melting Completion (Liquidus), °C 1380
1460
Melting Onset (Solidus), °C 1340
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 12
15
Thermal Expansion, µm/m-K 15
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 31
22
Density, g/cm3 8.0
7.9
Embodied Carbon, kg CO2/kg material 5.4
4.1
Embodied Energy, MJ/kg 76
57
Embodied Water, L/kg 190
180

Common Calculations

PREN (Pitting Resistance) 18
42
Resilience: Ultimate (Unit Rupture Work), MJ/m3 27
220
Resilience: Unit (Modulus of Resilience), kJ/m3 160
930
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 16
30
Strength to Weight: Bending, points 17
25
Thermal Diffusivity, mm2/s 3.1
4.0
Thermal Shock Resistance, points 11
23

Alloy Composition

Carbon (C), % 0.3 to 0.5
0 to 0.030
Chromium (Cr), % 16 to 18
24 to 26
Copper (Cu), % 0
0.5 to 1.0
Iron (Fe), % 40.4 to 48.7
57.6 to 65.8
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 0 to 0.5
3.0 to 4.0
Nickel (Ni), % 34 to 36
6.0 to 8.0
Nitrogen (N), % 0
0.2 to 0.3
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 1.0 to 2.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.010
Tungsten (W), % 0
0.5 to 1.0