EN 1.4806 Stainless Steel vs. S44536 Stainless Steel

Both EN 1.4806 stainless steel and S44536 stainless steel are iron alloys. They have 63% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4806 stainless steel and the bottom bar is S44536 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
170
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 6.8
22
Fatigue Strength, MPa 120
190
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 75
78
Tensile Strength: Ultimate (UTS), MPa 470
460
Tensile Strength: Yield (Proof), MPa 250
280

Thermal Properties

Latent Heat of Fusion, J/g 320
290
Maximum Temperature: Corrosion, °C 400
560
Maximum Temperature: Mechanical, °C 1000
990
Melting Completion (Liquidus), °C 1380
1440
Melting Onset (Solidus), °C 1340
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 12
21
Thermal Expansion, µm/m-K 15
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.6
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
3.0

Otherwise Unclassified Properties

Base Metal Price, % relative 31
13
Density, g/cm3 8.0
7.7
Embodied Carbon, kg CO2/kg material 5.4
2.8
Embodied Energy, MJ/kg 76
41
Embodied Water, L/kg 190
140

Common Calculations

PREN (Pitting Resistance) 18
22
Resilience: Ultimate (Unit Rupture Work), MJ/m3 27
89
Resilience: Unit (Modulus of Resilience), kJ/m3 160
200
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 16
17
Strength to Weight: Bending, points 17
17
Thermal Diffusivity, mm2/s 3.1
5.6
Thermal Shock Resistance, points 11
16

Alloy Composition

Carbon (C), % 0.3 to 0.5
0 to 0.015
Chromium (Cr), % 16 to 18
20 to 23
Iron (Fe), % 40.4 to 48.7
72.8 to 80
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 34 to 36
0 to 0.5
Niobium (Nb), % 0
0.050 to 0.8
Nitrogen (N), % 0
0 to 0.015
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 1.0 to 2.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030
Titanium (Ti), % 0
0 to 0.8