EN 1.4807 Stainless Steel vs. ASTM A225 Steel

Both EN 1.4807 stainless steel and ASTM A225 steel are iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4807 stainless steel and the bottom bar is ASTM A225 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
190 to 250
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 4.5
21 to 23
Fatigue Strength, MPa 120
330 to 390
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 75
73
Tensile Strength: Ultimate (UTS), MPa 480
620 to 830
Tensile Strength: Yield (Proof), MPa 250
460 to 550

Thermal Properties

Latent Heat of Fusion, J/g 320
250
Maximum Temperature: Mechanical, °C 1000
400
Melting Completion (Liquidus), °C 1390
1460
Melting Onset (Solidus), °C 1350
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 12
52
Thermal Expansion, µm/m-K 15
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 39
2.3
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 6.8
1.8
Embodied Energy, MJ/kg 97
24 to 25
Embodied Water, L/kg 190
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 18
120 to 170
Resilience: Unit (Modulus of Resilience), kJ/m3 160
580 to 820
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 17
22 to 29
Strength to Weight: Bending, points 17
21 to 25
Thermal Diffusivity, mm2/s 3.2
14
Thermal Shock Resistance, points 12
18 to 24