EN 1.4807 Stainless Steel vs. AWS E308L

Both EN 1.4807 stainless steel and AWS E308L are iron alloys. They have 72% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.4807 stainless steel and the bottom bar is AWS E308L.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 4.5
40
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 75
78
Tensile Strength: Ultimate (UTS), MPa 480
580

Thermal Properties

Latent Heat of Fusion, J/g 320
290
Melting Completion (Liquidus), °C 1390
1420
Melting Onset (Solidus), °C 1350
1380
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 12
16
Thermal Expansion, µm/m-K 15
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 39
16
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 6.8
3.2
Embodied Energy, MJ/kg 97
46
Embodied Water, L/kg 190
150

Common Calculations

PREN (Pitting Resistance) 19
21
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 17
21
Strength to Weight: Bending, points 17
20
Thermal Diffusivity, mm2/s 3.2
4.1
Thermal Shock Resistance, points 12
15

Alloy Composition

Carbon (C), % 0.3 to 0.5
0 to 0.040
Chromium (Cr), % 17 to 20
18 to 21
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 36.6 to 46.7
62.9 to 72.5
Manganese (Mn), % 0 to 2.0
0.5 to 2.5
Molybdenum (Mo), % 0 to 0.5
0 to 0.75
Nickel (Ni), % 34 to 36
9.0 to 11
Niobium (Nb), % 1.0 to 1.8
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 1.0 to 2.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030