EN 1.4807 Stainless Steel vs. AWS E383

Both EN 1.4807 stainless steel and AWS E383 are iron alloys. They have 86% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.4807 stainless steel and the bottom bar is AWS E383.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 4.5
34
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 75
80
Tensile Strength: Ultimate (UTS), MPa 480
580

Thermal Properties

Latent Heat of Fusion, J/g 320
320
Melting Completion (Liquidus), °C 1390
1420
Melting Onset (Solidus), °C 1350
1370
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 12
12
Thermal Expansion, µm/m-K 15
14

Otherwise Unclassified Properties

Base Metal Price, % relative 39
37
Density, g/cm3 8.0
8.1
Embodied Carbon, kg CO2/kg material 6.8
6.4
Embodied Energy, MJ/kg 97
89
Embodied Water, L/kg 190
240

Common Calculations

PREN (Pitting Resistance) 19
40
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 17
20
Strength to Weight: Bending, points 17
19
Thermal Diffusivity, mm2/s 3.2
3.1
Thermal Shock Resistance, points 12
15

Alloy Composition

Carbon (C), % 0.3 to 0.5
0 to 0.030
Chromium (Cr), % 17 to 20
26.5 to 29
Copper (Cu), % 0
0.6 to 1.5
Iron (Fe), % 36.6 to 46.7
28.8 to 39.2
Manganese (Mn), % 0 to 2.0
0.5 to 2.5
Molybdenum (Mo), % 0 to 0.5
3.2 to 4.2
Nickel (Ni), % 34 to 36
30 to 33
Niobium (Nb), % 1.0 to 1.8
0
Phosphorus (P), % 0 to 0.040
0 to 0.020
Silicon (Si), % 1.0 to 2.5
0 to 0.9
Sulfur (S), % 0 to 0.030
0 to 0.020