EN 1.4807 Stainless Steel vs. AWS E385

Both EN 1.4807 stainless steel and AWS E385 are iron alloys. They have 87% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.4807 stainless steel and the bottom bar is AWS E385.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 4.5
34
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 75
79
Tensile Strength: Ultimate (UTS), MPa 480
580

Thermal Properties

Latent Heat of Fusion, J/g 320
300
Melting Completion (Liquidus), °C 1390
1440
Melting Onset (Solidus), °C 1350
1390
Specific Heat Capacity, J/kg-K 480
460
Thermal Conductivity, W/m-K 12
14
Thermal Expansion, µm/m-K 15
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 39
31
Density, g/cm3 8.0
8.1
Embodied Carbon, kg CO2/kg material 6.8
5.8
Embodied Energy, MJ/kg 97
79
Embodied Water, L/kg 190
200

Common Calculations

PREN (Pitting Resistance) 19
36
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 17
20
Strength to Weight: Bending, points 17
19
Thermal Diffusivity, mm2/s 3.2
3.6
Thermal Shock Resistance, points 12
15

Alloy Composition

Carbon (C), % 0.3 to 0.5
0 to 0.030
Chromium (Cr), % 17 to 20
19.5 to 21.5
Copper (Cu), % 0
1.2 to 2.0
Iron (Fe), % 36.6 to 46.7
41.8 to 50.1
Manganese (Mn), % 0 to 2.0
1.0 to 2.5
Molybdenum (Mo), % 0 to 0.5
4.2 to 5.2
Nickel (Ni), % 34 to 36
24 to 26
Niobium (Nb), % 1.0 to 1.8
0
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 1.0 to 2.5
0 to 0.9
Sulfur (S), % 0 to 0.030
0 to 0.020