EN 1.4807 Stainless Steel vs. AWS ER110S-1

Both EN 1.4807 stainless steel and AWS ER110S-1 are iron alloys. They have 46% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4807 stainless steel and the bottom bar is AWS ER110S-1.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 4.5
17
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 75
73
Tensile Strength: Ultimate (UTS), MPa 480
870
Tensile Strength: Yield (Proof), MPa 250
740

Thermal Properties

Latent Heat of Fusion, J/g 320
250
Melting Completion (Liquidus), °C 1390
1460
Melting Onset (Solidus), °C 1350
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 12
47
Thermal Expansion, µm/m-K 15
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.7
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.8

Otherwise Unclassified Properties

Base Metal Price, % relative 39
4.0
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 6.8
1.8
Embodied Energy, MJ/kg 97
25
Embodied Water, L/kg 190
55

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 18
140
Resilience: Unit (Modulus of Resilience), kJ/m3 160
1460
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 17
31
Strength to Weight: Bending, points 17
26
Thermal Diffusivity, mm2/s 3.2
13
Thermal Shock Resistance, points 12
26

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
0 to 0.1
Carbon (C), % 0.3 to 0.5
0 to 0.090
Chromium (Cr), % 17 to 20
0 to 0.5
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 36.6 to 46.7
92.8 to 96.3
Manganese (Mn), % 0 to 2.0
1.4 to 1.8
Molybdenum (Mo), % 0 to 0.5
0.25 to 0.55
Nickel (Ni), % 34 to 36
1.9 to 2.6
Niobium (Nb), % 1.0 to 1.8
0
Phosphorus (P), % 0 to 0.040
0 to 0.010
Silicon (Si), % 1.0 to 2.5
0.2 to 0.55
Sulfur (S), % 0 to 0.030
0 to 0.010
Titanium (Ti), % 0
0 to 0.1
Vanadium (V), % 0
0 to 0.040
Zirconium (Zr), % 0
0 to 0.1
Residuals, % 0
0 to 0.5