EN 1.4807 Stainless Steel vs. EN 1.0215 Steel

Both EN 1.4807 stainless steel and EN 1.0215 steel are iron alloys. They have 42% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4807 stainless steel and the bottom bar is EN 1.0215 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
100
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 4.5
25
Fatigue Strength, MPa 120
180
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 75
73
Tensile Strength: Ultimate (UTS), MPa 480
350
Tensile Strength: Yield (Proof), MPa 250
250

Thermal Properties

Latent Heat of Fusion, J/g 320
250
Maximum Temperature: Mechanical, °C 1000
400
Melting Completion (Liquidus), °C 1390
1460
Melting Onset (Solidus), °C 1350
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 12
53
Thermal Expansion, µm/m-K 15
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 39
1.8
Density, g/cm3 8.0
7.9
Embodied Carbon, kg CO2/kg material 6.8
1.4
Embodied Energy, MJ/kg 97
18
Embodied Water, L/kg 190
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 18
79
Resilience: Unit (Modulus of Resilience), kJ/m3 160
160
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 17
13
Strength to Weight: Bending, points 17
14
Thermal Diffusivity, mm2/s 3.2
14
Thermal Shock Resistance, points 12
11

Alloy Composition

Carbon (C), % 0.3 to 0.5
0 to 0.14
Chromium (Cr), % 17 to 20
0
Iron (Fe), % 36.6 to 46.7
98.7 to 100
Manganese (Mn), % 0 to 2.0
0 to 0.7
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 34 to 36
0
Niobium (Nb), % 1.0 to 1.8
0
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 1.0 to 2.5
0 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.045