EN 1.4807 Stainless Steel vs. EN 1.0536 Steel

Both EN 1.4807 stainless steel and EN 1.0536 steel are iron alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 43% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4807 stainless steel and the bottom bar is EN 1.0536 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
210
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 4.5
18
Fatigue Strength, MPa 120
340
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 75
73
Tensile Strength: Ultimate (UTS), MPa 480
710
Tensile Strength: Yield (Proof), MPa 250
510

Thermal Properties

Latent Heat of Fusion, J/g 320
250
Maximum Temperature: Mechanical, °C 1000
400
Melting Completion (Liquidus), °C 1390
1460
Melting Onset (Solidus), °C 1350
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 12
51
Thermal Expansion, µm/m-K 15
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 39
2.1
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 6.8
1.7
Embodied Energy, MJ/kg 97
24
Embodied Water, L/kg 190
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 18
120
Resilience: Unit (Modulus of Resilience), kJ/m3 160
690
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 17
25
Strength to Weight: Bending, points 17
23
Thermal Diffusivity, mm2/s 3.2
14
Thermal Shock Resistance, points 12
22

Alloy Composition

Aluminum (Al), % 0
0.010 to 0.050
Carbon (C), % 0.3 to 0.5
0.16 to 0.22
Chromium (Cr), % 17 to 20
0
Iron (Fe), % 36.6 to 46.7
97.2 to 98.4
Manganese (Mn), % 0 to 2.0
1.3 to 1.7
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 34 to 36
0
Niobium (Nb), % 1.0 to 1.8
0 to 0.070
Nitrogen (N), % 0
0 to 0.020
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 1.0 to 2.5
0.1 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.035
Vanadium (V), % 0
0.080 to 0.15