EN 1.4807 Stainless Steel vs. EN 1.1244 Steel

Both EN 1.4807 stainless steel and EN 1.1244 steel are iron alloys. They have 43% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.4807 stainless steel and the bottom bar is EN 1.1244 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
210 to 220
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 75
72
Tensile Strength: Ultimate (UTS), MPa 480
730 to 770

Thermal Properties

Latent Heat of Fusion, J/g 320
250
Maximum Temperature: Mechanical, °C 1000
400
Melting Completion (Liquidus), °C 1390
1450
Melting Onset (Solidus), °C 1350
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 12
51
Thermal Expansion, µm/m-K 15
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 39
1.9
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 6.8
1.4
Embodied Energy, MJ/kg 97
19
Embodied Water, L/kg 190
47

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 17
26 to 28
Strength to Weight: Bending, points 17
23 to 24
Thermal Diffusivity, mm2/s 3.2
14
Thermal Shock Resistance, points 12
23 to 25

Alloy Composition

Aluminum (Al), % 0
0 to 0.050
Carbon (C), % 0.3 to 0.5
0.65 to 0.75
Chromium (Cr), % 17 to 20
0
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 36.6 to 46.7
98.1 to 99.2
Manganese (Mn), % 0 to 2.0
0.8 to 1.1
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 34 to 36
0
Niobium (Nb), % 1.0 to 1.8
0
Oxygen (O), % 0
0 to 0.0020
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 1.0 to 2.5
0 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.030