EN 1.4807 Stainless Steel vs. EN 1.3955 Stainless Steel

Both EN 1.4807 stainless steel and EN 1.3955 stainless steel are iron alloys. They have 72% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4807 stainless steel and the bottom bar is EN 1.3955 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 4.5
23
Fatigue Strength, MPa 120
150
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 75
77
Tensile Strength: Ultimate (UTS), MPa 480
520
Tensile Strength: Yield (Proof), MPa 250
220

Thermal Properties

Latent Heat of Fusion, J/g 320
290
Maximum Temperature: Corrosion, °C 600
410
Maximum Temperature: Mechanical, °C 1000
930
Melting Completion (Liquidus), °C 1390
1430
Melting Onset (Solidus), °C 1350
1380
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 12
15
Thermal Expansion, µm/m-K 15
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 39
16
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 6.8
3.2
Embodied Energy, MJ/kg 97
45
Embodied Water, L/kg 190
140

Common Calculations

PREN (Pitting Resistance) 19
19
Resilience: Ultimate (Unit Rupture Work), MJ/m3 18
95
Resilience: Unit (Modulus of Resilience), kJ/m3 160
130
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 17
18
Strength to Weight: Bending, points 17
18
Thermal Diffusivity, mm2/s 3.2
4.1
Thermal Shock Resistance, points 12
15

Alloy Composition

Carbon (C), % 0.3 to 0.5
0 to 0.15
Chromium (Cr), % 17 to 20
16.5 to 18.5
Iron (Fe), % 36.6 to 46.7
65.5 to 73.5
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 0 to 0.5
0 to 0.75
Nickel (Ni), % 34 to 36
10 to 12
Niobium (Nb), % 1.0 to 1.8
0
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 1.0 to 2.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030