EN 1.4807 Stainless Steel vs. EN 1.4005 Stainless Steel

Both EN 1.4807 stainless steel and EN 1.4005 stainless steel are iron alloys. They have 56% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4807 stainless steel and the bottom bar is EN 1.4005 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 4.5
13 to 21
Fatigue Strength, MPa 120
240 to 290
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 75
76
Tensile Strength: Ultimate (UTS), MPa 480
630 to 750
Tensile Strength: Yield (Proof), MPa 250
370 to 500

Thermal Properties

Latent Heat of Fusion, J/g 320
270
Maximum Temperature: Corrosion, °C 600
390
Maximum Temperature: Mechanical, °C 1000
760
Melting Completion (Liquidus), °C 1390
1440
Melting Onset (Solidus), °C 1350
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 12
30
Thermal Expansion, µm/m-K 15
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 39
7.0
Density, g/cm3 8.0
7.7
Embodied Carbon, kg CO2/kg material 6.8
2.0
Embodied Energy, MJ/kg 97
28
Embodied Water, L/kg 190
100

Common Calculations

PREN (Pitting Resistance) 19
14
Resilience: Ultimate (Unit Rupture Work), MJ/m3 18
90 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 160
350 to 650
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 17
23 to 27
Strength to Weight: Bending, points 17
21 to 24
Thermal Diffusivity, mm2/s 3.2
8.1
Thermal Shock Resistance, points 12
23 to 27

Alloy Composition

Carbon (C), % 0.3 to 0.5
0.060 to 0.15
Chromium (Cr), % 17 to 20
12 to 14
Iron (Fe), % 36.6 to 46.7
82.4 to 87.8
Manganese (Mn), % 0 to 2.0
0 to 1.5
Molybdenum (Mo), % 0 to 0.5
0 to 0.6
Nickel (Ni), % 34 to 36
0
Niobium (Nb), % 1.0 to 1.8
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 1.0 to 2.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0.15 to 0.35