EN 1.4807 Stainless Steel vs. EN 1.5023 Steel

Both EN 1.4807 stainless steel and EN 1.5023 steel are iron alloys. They have 44% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.4807 stainless steel and the bottom bar is EN 1.5023 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
170 to 440
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 75
72
Tensile Strength: Ultimate (UTS), MPa 480
570 to 1860

Thermal Properties

Latent Heat of Fusion, J/g 320
270
Maximum Temperature: Mechanical, °C 1000
400
Melting Completion (Liquidus), °C 1390
1440
Melting Onset (Solidus), °C 1350
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 12
48
Thermal Expansion, µm/m-K 15
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 39
1.9
Density, g/cm3 8.0
7.7
Embodied Carbon, kg CO2/kg material 6.8
1.4
Embodied Energy, MJ/kg 97
19
Embodied Water, L/kg 190
45

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 17
21 to 67
Strength to Weight: Bending, points 17
20 to 43
Thermal Diffusivity, mm2/s 3.2
13
Thermal Shock Resistance, points 12
17 to 56

Alloy Composition

Carbon (C), % 0.3 to 0.5
0.35 to 0.42
Chromium (Cr), % 17 to 20
0
Iron (Fe), % 36.6 to 46.7
96.9 to 97.7
Manganese (Mn), % 0 to 2.0
0.5 to 0.8
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 34 to 36
0
Niobium (Nb), % 1.0 to 1.8
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 1.0 to 2.5
1.5 to 1.8
Sulfur (S), % 0 to 0.030
0 to 0.025