EN 1.4807 Stainless Steel vs. SAE-AISI M48 Steel

Both EN 1.4807 stainless steel and SAE-AISI M48 steel are iron alloys. They have 47% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is EN 1.4807 stainless steel and the bottom bar is SAE-AISI M48 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 75
78
Tensile Strength: Ultimate (UTS), MPa 480
890 to 2390

Thermal Properties

Latent Heat of Fusion, J/g 320
260
Melting Completion (Liquidus), °C 1390
1670
Melting Onset (Solidus), °C 1350
1620
Specific Heat Capacity, J/kg-K 480
420
Thermal Expansion, µm/m-K 15
12

Otherwise Unclassified Properties

Base Metal Price, % relative 39
48
Density, g/cm3 8.0
8.7
Embodied Carbon, kg CO2/kg material 6.8
13
Embodied Energy, MJ/kg 97
190
Embodied Water, L/kg 190
160

Common Calculations

PREN (Pitting Resistance) 19
37
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
22
Strength to Weight: Axial, points 17
28 to 76
Strength to Weight: Bending, points 17
23 to 45
Thermal Shock Resistance, points 12
26 to 71

Alloy Composition

Carbon (C), % 0.3 to 0.5
1.4 to 1.5
Chromium (Cr), % 17 to 20
3.5 to 4.0
Cobalt (Co), % 0
8.0 to 10
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 36.6 to 46.7
63.8 to 69.8
Manganese (Mn), % 0 to 2.0
0.15 to 0.4
Molybdenum (Mo), % 0 to 0.5
4.8 to 5.5
Nickel (Ni), % 34 to 36
0 to 0.3
Niobium (Nb), % 1.0 to 1.8
0
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 1.0 to 2.5
0.15 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 0
9.5 to 10.5
Vanadium (V), % 0
2.8 to 3.3