EN 1.4807 Stainless Steel vs. N08135 Stainless Steel

Both EN 1.4807 stainless steel and N08135 stainless steel are iron alloys. They have a moderately high 91% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.4807 stainless steel and the bottom bar is N08135 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 4.5
46
Fatigue Strength, MPa 120
220
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 75
80
Tensile Strength: Ultimate (UTS), MPa 480
570
Tensile Strength: Yield (Proof), MPa 250
240

Thermal Properties

Latent Heat of Fusion, J/g 320
310
Maximum Temperature: Corrosion, °C 600
430
Maximum Temperature: Mechanical, °C 1000
1100
Melting Completion (Liquidus), °C 1390
1440
Melting Onset (Solidus), °C 1350
1390
Specific Heat Capacity, J/kg-K 480
460
Thermal Expansion, µm/m-K 15
16

Otherwise Unclassified Properties

Base Metal Price, % relative 39
39
Density, g/cm3 8.0
8.2
Embodied Carbon, kg CO2/kg material 6.8
6.8
Embodied Energy, MJ/kg 97
94
Embodied Water, L/kg 190
220

Common Calculations

PREN (Pitting Resistance) 19
38
Resilience: Ultimate (Unit Rupture Work), MJ/m3 18
210
Resilience: Unit (Modulus of Resilience), kJ/m3 160
140
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 17
19
Strength to Weight: Bending, points 17
19
Thermal Shock Resistance, points 12
13

Alloy Composition

Carbon (C), % 0.3 to 0.5
0 to 0.030
Chromium (Cr), % 17 to 20
20.5 to 23.5
Copper (Cu), % 0
0 to 0.7
Iron (Fe), % 36.6 to 46.7
30.2 to 42.3
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 0 to 0.5
4.0 to 5.0
Nickel (Ni), % 34 to 36
33 to 38
Niobium (Nb), % 1.0 to 1.8
0
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 1.0 to 2.5
0 to 0.75
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 0
0.2 to 0.8