EN 1.4807 Stainless Steel vs. S32101 Stainless Steel

Both EN 1.4807 stainless steel and S32101 stainless steel are iron alloys. They have 64% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4807 stainless steel and the bottom bar is S32101 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
260
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 4.5
34
Fatigue Strength, MPa 120
400
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 75
78
Tensile Strength: Ultimate (UTS), MPa 480
740
Tensile Strength: Yield (Proof), MPa 250
500

Thermal Properties

Latent Heat of Fusion, J/g 320
290
Maximum Temperature: Corrosion, °C 600
430
Maximum Temperature: Mechanical, °C 1000
1000
Melting Completion (Liquidus), °C 1390
1420
Melting Onset (Solidus), °C 1350
1370
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 12
15
Thermal Expansion, µm/m-K 15
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 39
12
Density, g/cm3 8.0
7.7
Embodied Carbon, kg CO2/kg material 6.8
2.6
Embodied Energy, MJ/kg 97
38
Embodied Water, L/kg 190
150

Common Calculations

PREN (Pitting Resistance) 19
27
Resilience: Ultimate (Unit Rupture Work), MJ/m3 18
230
Resilience: Unit (Modulus of Resilience), kJ/m3 160
640
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 17
27
Strength to Weight: Bending, points 17
24
Thermal Diffusivity, mm2/s 3.2
4.0
Thermal Shock Resistance, points 12
20

Alloy Composition

Carbon (C), % 0.3 to 0.5
0 to 0.040
Chromium (Cr), % 17 to 20
21 to 22
Copper (Cu), % 0
0.1 to 0.8
Iron (Fe), % 36.6 to 46.7
67.3 to 73.3
Manganese (Mn), % 0 to 2.0
4.0 to 6.0
Molybdenum (Mo), % 0 to 0.5
0.1 to 0.8
Nickel (Ni), % 34 to 36
1.4 to 1.7
Niobium (Nb), % 1.0 to 1.8
0
Nitrogen (N), % 0
0.2 to 0.25
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 1.0 to 2.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030