EN 1.4807 Stainless Steel vs. S32950 Stainless Steel

Both EN 1.4807 stainless steel and S32950 stainless steel are iron alloys. They have 66% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4807 stainless steel and the bottom bar is S32950 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
260
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 4.5
17
Fatigue Strength, MPa 120
330
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 75
80
Tensile Strength: Ultimate (UTS), MPa 480
780
Tensile Strength: Yield (Proof), MPa 250
550

Thermal Properties

Latent Heat of Fusion, J/g 320
300
Maximum Temperature: Corrosion, °C 600
460
Maximum Temperature: Mechanical, °C 1000
1100
Melting Completion (Liquidus), °C 1390
1430
Melting Onset (Solidus), °C 1350
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 12
16
Thermal Expansion, µm/m-K 15
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 39
17
Density, g/cm3 8.0
7.7
Embodied Carbon, kg CO2/kg material 6.8
3.4
Embodied Energy, MJ/kg 97
47
Embodied Water, L/kg 190
180

Common Calculations

PREN (Pitting Resistance) 19
37
Resilience: Ultimate (Unit Rupture Work), MJ/m3 18
120
Resilience: Unit (Modulus of Resilience), kJ/m3 160
730
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 17
28
Strength to Weight: Bending, points 17
24
Thermal Diffusivity, mm2/s 3.2
4.3
Thermal Shock Resistance, points 12
21

Alloy Composition

Carbon (C), % 0.3 to 0.5
0 to 0.030
Chromium (Cr), % 17 to 20
26 to 29
Iron (Fe), % 36.6 to 46.7
60.3 to 69.4
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 0 to 0.5
1.0 to 2.5
Nickel (Ni), % 34 to 36
3.5 to 5.2
Niobium (Nb), % 1.0 to 1.8
0
Nitrogen (N), % 0
0.15 to 0.35
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 1.0 to 2.5
0 to 0.6
Sulfur (S), % 0 to 0.030
0 to 0.010