EN 1.4807 Stainless Steel vs. S35500 Stainless Steel

Both EN 1.4807 stainless steel and S35500 stainless steel are iron alloys. They have 64% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4807 stainless steel and the bottom bar is S35500 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 4.5
14
Fatigue Strength, MPa 120
690 to 730
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 75
78
Tensile Strength: Ultimate (UTS), MPa 480
1330 to 1490
Tensile Strength: Yield (Proof), MPa 250
1200 to 1280

Thermal Properties

Latent Heat of Fusion, J/g 320
280
Maximum Temperature: Corrosion, °C 600
440
Maximum Temperature: Mechanical, °C 1000
870
Melting Completion (Liquidus), °C 1390
1460
Melting Onset (Solidus), °C 1350
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 12
16
Thermal Expansion, µm/m-K 15
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 39
16
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 6.8
3.5
Embodied Energy, MJ/kg 97
47
Embodied Water, L/kg 190
130

Common Calculations

PREN (Pitting Resistance) 19
27
Resilience: Ultimate (Unit Rupture Work), MJ/m3 18
180 to 190
Resilience: Unit (Modulus of Resilience), kJ/m3 160
3610 to 4100
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 17
47 to 53
Strength to Weight: Bending, points 17
34 to 37
Thermal Diffusivity, mm2/s 3.2
4.4
Thermal Shock Resistance, points 12
44 to 49

Alloy Composition

Carbon (C), % 0.3 to 0.5
0.1 to 0.15
Chromium (Cr), % 17 to 20
15 to 16
Iron (Fe), % 36.6 to 46.7
73.2 to 77.7
Manganese (Mn), % 0 to 2.0
0.5 to 1.3
Molybdenum (Mo), % 0 to 0.5
2.5 to 3.2
Nickel (Ni), % 34 to 36
4.0 to 5.0
Niobium (Nb), % 1.0 to 1.8
0.1 to 0.5
Nitrogen (N), % 0
0.070 to 0.13
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 1.0 to 2.5
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.030