EN 1.4826 stainless steel belongs to the iron alloys classification, while 90-silver 10-nickel belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is EN 1.4826 stainless steel and the bottom bar is 90-silver 10-nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
82
Poisson's Ratio 0.28
0.36
Shear Modulus, GPa 77
30
Tensile Strength: Ultimate (UTS), MPa 500
250 to 420

Thermal Properties

Latent Heat of Fusion, J/g 310
130
Melting Completion (Liquidus), °C 1400
840
Melting Onset (Solidus), °C 1360
960
Specific Heat Capacity, J/kg-K 490
260
Thermal Expansion, µm/m-K 16
19

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
90
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
79

Otherwise Unclassified Properties

Density, g/cm3 7.7
10

Common Calculations

Stiffness to Weight: Axial, points 14
4.4
Stiffness to Weight: Bending, points 25
14
Strength to Weight: Axial, points 18
6.7 to 11
Strength to Weight: Bending, points 18
8.5 to 12
Thermal Shock Resistance, points 11
11 to 19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0.3 to 0.5
0
Chromium (Cr), % 21 to 23
0
Iron (Fe), % 60.4 to 68.7
0
Manganese (Mn), % 0 to 2.0
0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 9.0 to 11
8.8 to 11
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 1.0 to 2.5
0
Silver (Ag), % 0
89 to 91
Sulfur (S), % 0 to 0.030
0
Residuals, % 0
0 to 0.2