EN 1.4826 Stainless Steel vs. ACI-ASTM CH20 Steel

Both EN 1.4826 stainless steel and ACI-ASTM CH20 steel are iron alloys. They have a moderately high 94% of their average alloy composition in common.

For each property being compared, the top bar is EN 1.4826 stainless steel and the bottom bar is ACI-ASTM CH20 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
190
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 9.1
38
Fatigue Strength, MPa 140
290
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 77
78
Tensile Strength: Ultimate (UTS), MPa 500
610
Tensile Strength: Yield (Proof), MPa 260
350

Thermal Properties

Latent Heat of Fusion, J/g 310
310
Maximum Temperature: Corrosion, °C 430
440
Maximum Temperature: Mechanical, °C 950
1100
Melting Completion (Liquidus), °C 1400
1410
Melting Onset (Solidus), °C 1360
1430
Specific Heat Capacity, J/kg-K 490
480
Thermal Conductivity, W/m-K 14
14
Thermal Expansion, µm/m-K 16
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 17
20
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 3.3
3.7
Embodied Energy, MJ/kg 47
53
Embodied Water, L/kg 160
180

Common Calculations

PREN (Pitting Resistance) 23
25
Resilience: Ultimate (Unit Rupture Work), MJ/m3 39
200
Resilience: Unit (Modulus of Resilience), kJ/m3 170
300
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 18
22
Strength to Weight: Bending, points 18
21
Thermal Diffusivity, mm2/s 3.7
3.7
Thermal Shock Resistance, points 11
15

Alloy Composition

Carbon (C), % 0.3 to 0.5
0 to 0.2
Chromium (Cr), % 21 to 23
22 to 26
Iron (Fe), % 60.4 to 68.7
54.7 to 66
Manganese (Mn), % 0 to 2.0
0 to 1.5
Molybdenum (Mo), % 0 to 0.5
0 to 0.5
Nickel (Ni), % 9.0 to 11
12 to 15
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 1.0 to 2.5
0 to 2.0
Sulfur (S), % 0 to 0.030
0 to 0.040