EN 1.4826 Stainless Steel vs. ASTM B477 Au-Ni-Ag

EN 1.4826 stainless steel belongs to the iron alloys classification, while ASTM B477 Au-Ni-Ag belongs to the otherwise unclassified metals. There are 18 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN 1.4826 stainless steel and the bottom bar is ASTM B477 Au-Ni-Ag.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
95
Elongation at Break, % 9.1
5.5 to 11
Poisson's Ratio 0.28
0.41
Shear Modulus, GPa 77
34
Tensile Strength: Ultimate (UTS), MPa 500
310 to 550

Thermal Properties

Latent Heat of Fusion, J/g 310
80
Melting Completion (Liquidus), °C 1400
1010
Melting Onset (Solidus), °C 1360
930
Specific Heat Capacity, J/kg-K 490
160
Thermal Expansion, µm/m-K 16
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
14
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
7.5

Otherwise Unclassified Properties

Density, g/cm3 7.7
17

Common Calculations

Stiffness to Weight: Axial, points 14
3.1
Stiffness to Weight: Bending, points 25
8.9
Strength to Weight: Axial, points 18
5.0 to 9.0
Strength to Weight: Bending, points 18
6.0 to 8.8
Thermal Shock Resistance, points 11
16 to 28

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0.3 to 0.5
0
Chromium (Cr), % 21 to 23
0
Gold (Au), % 0
74.2 to 75.8
Iron (Fe), % 60.4 to 68.7
0
Manganese (Mn), % 0 to 2.0
0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 9.0 to 11
2.6 to 3.4
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 1.0 to 2.5
0
Silver (Ag), % 0
21.4 to 22.6
Sulfur (S), % 0 to 0.030
0
Residuals, % 0
0 to 0.3