EN 1.4826 Stainless Steel vs. AWS BAg-35

EN 1.4826 stainless steel belongs to the iron alloys classification, while AWS BAg-35 belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is EN 1.4826 stainless steel and the bottom bar is AWS BAg-35.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
91
Poisson's Ratio 0.28
0.32
Shear Modulus, GPa 77
34
Tensile Strength: Ultimate (UTS), MPa 500
170

Thermal Properties

Latent Heat of Fusion, J/g 310
140
Melting Completion (Liquidus), °C 1400
750
Melting Onset (Solidus), °C 1360
690
Specific Heat Capacity, J/kg-K 490
330
Thermal Expansion, µm/m-K 16
21

Otherwise Unclassified Properties

Density, g/cm3 7.7
8.7
Embodied Carbon, kg CO2/kg material 3.3
35
Embodied Energy, MJ/kg 47
550

Common Calculations

Stiffness to Weight: Axial, points 14
5.8
Stiffness to Weight: Bending, points 25
17
Strength to Weight: Axial, points 18
5.4
Strength to Weight: Bending, points 18
7.8
Thermal Shock Resistance, points 11
6.4

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0.3 to 0.5
0
Chromium (Cr), % 21 to 23
0
Copper (Cu), % 0
31 to 33
Iron (Fe), % 60.4 to 68.7
0
Manganese (Mn), % 0 to 2.0
0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 9.0 to 11
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 1.0 to 2.5
0
Silver (Ag), % 0
34 to 36
Sulfur (S), % 0 to 0.030
0
Zinc (Zn), % 0
31 to 35
Residuals, % 0
0 to 0.15