EN 1.4826 Stainless Steel vs. Class 3 Tungsten

EN 1.4826 stainless steel belongs to the iron alloys classification, while class 3 tungsten belongs to the otherwise unclassified metals. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.4826 stainless steel and the bottom bar is class 3 tungsten.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
270
Elongation at Break, % 9.1
3.4
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
100
Tensile Strength: Ultimate (UTS), MPa 500
830
Tensile Strength: Yield (Proof), MPa 260
580

Thermal Properties

Latent Heat of Fusion, J/g 310
170
Specific Heat Capacity, J/kg-K 490
120
Thermal Conductivity, W/m-K 14
30
Thermal Expansion, µm/m-K 16
4.5

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
15
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.5

Otherwise Unclassified Properties

Density, g/cm3 7.7
15
Embodied Carbon, kg CO2/kg material 3.3
23
Embodied Energy, MJ/kg 47
360
Embodied Water, L/kg 160
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 39
25
Resilience: Unit (Modulus of Resilience), kJ/m3 170
630
Stiffness to Weight: Axial, points 14
9.6
Stiffness to Weight: Bending, points 25
14
Strength to Weight: Axial, points 18
15
Strength to Weight: Bending, points 18
13
Thermal Diffusivity, mm2/s 3.7
15
Thermal Shock Resistance, points 11
49

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0.3 to 0.5
0
Chromium (Cr), % 21 to 23
0
Iron (Fe), % 60.4 to 68.7
0
Manganese (Mn), % 0 to 2.0
0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 9.0 to 11
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 1.0 to 2.5
0
Sulfur (S), % 0 to 0.030
0
Tungsten (W), % 0
95
Residuals, % 0
5.0