EN 1.4826 Stainless Steel vs. EN 1.3967 Stainless Steel

Both EN 1.4826 stainless steel and EN 1.3967 stainless steel are iron alloys. They have 87% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4826 stainless steel and the bottom bar is EN 1.3967 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
200
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 9.1
22
Fatigue Strength, MPa 140
240
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
79
Tensile Strength: Ultimate (UTS), MPa 500
690
Tensile Strength: Yield (Proof), MPa 260
350

Thermal Properties

Latent Heat of Fusion, J/g 310
300
Maximum Temperature: Corrosion, °C 430
440
Maximum Temperature: Mechanical, °C 950
1070
Melting Completion (Liquidus), °C 1400
1430
Melting Onset (Solidus), °C 1360
1380
Specific Heat Capacity, J/kg-K 490
470
Thermal Expansion, µm/m-K 16
16

Otherwise Unclassified Properties

Base Metal Price, % relative 17
25
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 3.3
4.8
Embodied Energy, MJ/kg 47
66
Embodied Water, L/kg 160
180

Common Calculations

PREN (Pitting Resistance) 23
36
Resilience: Ultimate (Unit Rupture Work), MJ/m3 39
130
Resilience: Unit (Modulus of Resilience), kJ/m3 170
310
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 18
24
Strength to Weight: Bending, points 18
22
Thermal Shock Resistance, points 11
15

Alloy Composition

Carbon (C), % 0.3 to 0.5
0 to 0.030
Chromium (Cr), % 21 to 23
20 to 21.5
Iron (Fe), % 60.4 to 68.7
50.3 to 57.8
Manganese (Mn), % 0 to 2.0
4.0 to 6.0
Molybdenum (Mo), % 0 to 0.5
3.0 to 3.5
Nickel (Ni), % 9.0 to 11
15 to 17
Niobium (Nb), % 0
0 to 0.25
Nitrogen (N), % 0
0.2 to 0.35
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 1.0 to 2.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.010