EN 1.4826 Stainless Steel vs. EN 1.4307 Stainless Steel

Both EN 1.4826 stainless steel and EN 1.4307 stainless steel are iron alloys. They have a moderately high 94% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4826 stainless steel and the bottom bar is EN 1.4307 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
180 to 270
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 9.1
14 to 46
Fatigue Strength, MPa 140
190 to 320
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
77
Tensile Strength: Ultimate (UTS), MPa 500
590 to 900
Tensile Strength: Yield (Proof), MPa 260
200 to 570

Thermal Properties

Latent Heat of Fusion, J/g 310
290
Maximum Temperature: Corrosion, °C 430
420
Maximum Temperature: Mechanical, °C 950
940
Melting Completion (Liquidus), °C 1400
1430
Melting Onset (Solidus), °C 1360
1380
Specific Heat Capacity, J/kg-K 490
480
Thermal Conductivity, W/m-K 14
15
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 17
15
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 3.3
3.0
Embodied Energy, MJ/kg 47
43
Embodied Water, L/kg 160
140

Common Calculations

PREN (Pitting Resistance) 23
19
Resilience: Ultimate (Unit Rupture Work), MJ/m3 39
110 to 210
Resilience: Unit (Modulus of Resilience), kJ/m3 170
100 to 810
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 18
21 to 32
Strength to Weight: Bending, points 18
20 to 27
Thermal Diffusivity, mm2/s 3.7
4.0
Thermal Shock Resistance, points 11
13 to 20

Alloy Composition

Carbon (C), % 0.3 to 0.5
0 to 0.030
Chromium (Cr), % 21 to 23
17.5 to 19.5
Iron (Fe), % 60.4 to 68.7
66.8 to 74.5
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 9.0 to 11
8.0 to 10.5
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 1.0 to 2.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015