EN 1.4826 Stainless Steel vs. EN 1.4308 Stainless Steel

Both EN 1.4826 stainless steel and EN 1.4308 stainless steel are iron alloys. They have a moderately high 95% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4826 stainless steel and the bottom bar is EN 1.4308 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
150
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 9.1
34
Fatigue Strength, MPa 140
160
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
77
Tensile Strength: Ultimate (UTS), MPa 500
510
Tensile Strength: Yield (Proof), MPa 260
200

Thermal Properties

Latent Heat of Fusion, J/g 310
290
Maximum Temperature: Corrosion, °C 430
420
Maximum Temperature: Mechanical, °C 950
960
Melting Completion (Liquidus), °C 1400
1420
Melting Onset (Solidus), °C 1360
1380
Specific Heat Capacity, J/kg-K 490
480
Thermal Conductivity, W/m-K 14
15
Thermal Expansion, µm/m-K 16
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 17
15
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 3.3
3.0
Embodied Energy, MJ/kg 47
43
Embodied Water, L/kg 160
150

Common Calculations

PREN (Pitting Resistance) 23
19
Resilience: Ultimate (Unit Rupture Work), MJ/m3 39
140
Resilience: Unit (Modulus of Resilience), kJ/m3 170
100
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 18
18
Strength to Weight: Bending, points 18
18
Thermal Diffusivity, mm2/s 3.7
4.1
Thermal Shock Resistance, points 11
11

Alloy Composition

Carbon (C), % 0.3 to 0.5
0 to 0.070
Chromium (Cr), % 21 to 23
18 to 20
Iron (Fe), % 60.4 to 68.7
65.9 to 74
Manganese (Mn), % 0 to 2.0
0 to 1.5
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 9.0 to 11
8.0 to 11
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 1.0 to 2.5
0 to 1.5
Sulfur (S), % 0 to 0.030
0 to 0.030