EN 1.4826 Stainless Steel vs. EN 1.4405 Stainless Steel

Both EN 1.4826 stainless steel and EN 1.4405 stainless steel are iron alloys. They have 87% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4826 stainless steel and the bottom bar is EN 1.4405 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 9.1
17
Fatigue Strength, MPa 140
370
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
77
Tensile Strength: Ultimate (UTS), MPa 500
860
Tensile Strength: Yield (Proof), MPa 260
610

Thermal Properties

Latent Heat of Fusion, J/g 310
280
Maximum Temperature: Corrosion, °C 430
410
Maximum Temperature: Mechanical, °C 950
870
Melting Completion (Liquidus), °C 1400
1450
Melting Onset (Solidus), °C 1360
1400
Specific Heat Capacity, J/kg-K 490
480
Thermal Conductivity, W/m-K 14
17
Thermal Expansion, µm/m-K 16
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 17
13
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 3.3
2.8
Embodied Energy, MJ/kg 47
39
Embodied Water, L/kg 160
130

Common Calculations

PREN (Pitting Resistance) 23
20
Resilience: Ultimate (Unit Rupture Work), MJ/m3 39
130
Resilience: Unit (Modulus of Resilience), kJ/m3 170
950
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 18
31
Strength to Weight: Bending, points 18
26
Thermal Diffusivity, mm2/s 3.7
4.6
Thermal Shock Resistance, points 11
29

Alloy Composition

Carbon (C), % 0.3 to 0.5
0 to 0.060
Chromium (Cr), % 21 to 23
15 to 17
Iron (Fe), % 60.4 to 68.7
73.6 to 80.3
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 0 to 0.5
0.7 to 1.5
Nickel (Ni), % 9.0 to 11
4.0 to 6.0
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 1.0 to 2.5
0 to 0.8
Sulfur (S), % 0 to 0.030
0 to 0.025