EN 1.4826 Stainless Steel vs. EN 1.4435 Stainless Steel

Both EN 1.4826 stainless steel and EN 1.4435 stainless steel are iron alloys. They have a moderately high 94% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4826 stainless steel and the bottom bar is EN 1.4435 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
190
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 9.1
43
Fatigue Strength, MPa 140
220
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
78
Tensile Strength: Ultimate (UTS), MPa 500
610
Tensile Strength: Yield (Proof), MPa 260
240

Thermal Properties

Latent Heat of Fusion, J/g 310
290
Maximum Temperature: Corrosion, °C 430
420
Maximum Temperature: Mechanical, °C 950
980
Melting Completion (Liquidus), °C 1400
1440
Melting Onset (Solidus), °C 1360
1400
Specific Heat Capacity, J/kg-K 490
470
Thermal Conductivity, W/m-K 14
15
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 17
21
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 3.3
4.1
Embodied Energy, MJ/kg 47
57
Embodied Water, L/kg 160
160

Common Calculations

PREN (Pitting Resistance) 23
28
Resilience: Ultimate (Unit Rupture Work), MJ/m3 39
210
Resilience: Unit (Modulus of Resilience), kJ/m3 170
150
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 18
21
Strength to Weight: Bending, points 18
20
Thermal Diffusivity, mm2/s 3.7
4.0
Thermal Shock Resistance, points 11
14

Alloy Composition

Carbon (C), % 0.3 to 0.5
0 to 0.030
Chromium (Cr), % 21 to 23
17 to 19
Iron (Fe), % 60.4 to 68.7
59.8 to 68
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 0 to 0.5
2.5 to 3.0
Nickel (Ni), % 9.0 to 11
12.5 to 15
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 1.0 to 2.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015