EN 1.4826 Stainless Steel vs. EN 1.4460 Stainless Steel

Both EN 1.4826 stainless steel and EN 1.4460 stainless steel are iron alloys. They have a moderately high 94% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4826 stainless steel and the bottom bar is EN 1.4460 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
220
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 9.1
21
Fatigue Strength, MPa 140
330
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 77
80
Tensile Strength: Ultimate (UTS), MPa 500
750
Tensile Strength: Yield (Proof), MPa 260
510

Thermal Properties

Latent Heat of Fusion, J/g 310
300
Maximum Temperature: Corrosion, °C 430
450
Maximum Temperature: Mechanical, °C 950
1100
Melting Completion (Liquidus), °C 1400
1430
Melting Onset (Solidus), °C 1360
1390
Specific Heat Capacity, J/kg-K 490
480
Thermal Conductivity, W/m-K 14
15
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 17
18
Density, g/cm3 7.7
7.7
Embodied Carbon, kg CO2/kg material 3.3
3.4
Embodied Energy, MJ/kg 47
48
Embodied Water, L/kg 160
180

Common Calculations

PREN (Pitting Resistance) 23
34
Resilience: Ultimate (Unit Rupture Work), MJ/m3 39
140
Resilience: Unit (Modulus of Resilience), kJ/m3 170
640
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 18
27
Strength to Weight: Bending, points 18
24
Thermal Diffusivity, mm2/s 3.7
4.0
Thermal Shock Resistance, points 11
20

Alloy Composition

Carbon (C), % 0.3 to 0.5
0 to 0.050
Chromium (Cr), % 21 to 23
25 to 28
Iron (Fe), % 60.4 to 68.7
60.2 to 69.2
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 0 to 0.5
1.3 to 2.0
Nickel (Ni), % 9.0 to 11
4.5 to 6.5
Nitrogen (N), % 0
0.050 to 0.2
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 1.0 to 2.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015