EN 1.4826 Stainless Steel vs. EN 1.4919 Stainless Steel

Both EN 1.4826 stainless steel and EN 1.4919 stainless steel are iron alloys. They have a moderately high 94% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4826 stainless steel and the bottom bar is EN 1.4919 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
180
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 9.1
40
Fatigue Strength, MPa 140
200
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
78
Tensile Strength: Ultimate (UTS), MPa 500
590
Tensile Strength: Yield (Proof), MPa 260
230

Thermal Properties

Latent Heat of Fusion, J/g 310
290
Maximum Temperature: Corrosion, °C 430
410
Maximum Temperature: Mechanical, °C 950
950
Melting Completion (Liquidus), °C 1400
1440
Melting Onset (Solidus), °C 1360
1400
Specific Heat Capacity, J/kg-K 490
470
Thermal Conductivity, W/m-K 14
16
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 17
19
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 3.3
3.8
Embodied Energy, MJ/kg 47
52
Embodied Water, L/kg 160
150

Common Calculations

PREN (Pitting Resistance) 23
26
Resilience: Ultimate (Unit Rupture Work), MJ/m3 39
190
Resilience: Unit (Modulus of Resilience), kJ/m3 170
130
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 18
21
Strength to Weight: Bending, points 18
20
Thermal Diffusivity, mm2/s 3.7
4.3
Thermal Shock Resistance, points 11
13

Alloy Composition

Boron (B), % 0
0.0015 to 0.0050
Carbon (C), % 0.3 to 0.5
0.040 to 0.080
Chromium (Cr), % 21 to 23
16.5 to 18.5
Iron (Fe), % 60.4 to 68.7
62.8 to 71.5
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 0 to 0.5
2.0 to 2.5
Nickel (Ni), % 9.0 to 11
10 to 13
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 1.0 to 2.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015