EN 1.4826 Stainless Steel vs. Solder Alloy 113

EN 1.4826 stainless steel belongs to the iron alloys classification, while solder alloy 113 belongs to the otherwise unclassified metals. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.4826 stainless steel and the bottom bar is solder alloy 113.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
32
Elongation at Break, % 9.1
32
Poisson's Ratio 0.28
0.4
Shear Modulus, GPa 77
11
Tensile Strength: Ultimate (UTS), MPa 500
39

Thermal Properties

Latent Heat of Fusion, J/g 310
40
Melting Completion (Liquidus), °C 1400
230
Melting Onset (Solidus), °C 1360
180
Specific Heat Capacity, J/kg-K 490
170
Thermal Conductivity, W/m-K 14
46
Thermal Expansion, µm/m-K 16
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
10
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
9.8

Otherwise Unclassified Properties

Density, g/cm3 7.7
9.5
Embodied Carbon, kg CO2/kg material 3.3
8.9
Embodied Energy, MJ/kg 47
150
Embodied Water, L/kg 160
800

Common Calculations

Stiffness to Weight: Axial, points 14
1.8
Stiffness to Weight: Bending, points 25
11
Strength to Weight: Axial, points 18
1.1
Strength to Weight: Bending, points 18
2.7
Thermal Diffusivity, mm2/s 3.7
28
Thermal Shock Resistance, points 11
3.4

Alloy Composition

Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.5
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.25
Cadmium (Cd), % 0
0 to 0.0050
Carbon (C), % 0.3 to 0.5
0
Chromium (Cr), % 21 to 23
0
Copper (Cu), % 0
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 60.4 to 68.7
0 to 0.020
Lead (Pb), % 0
53.4 to 55.5
Manganese (Mn), % 0 to 2.0
0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 9.0 to 11
0 to 0.010
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 1.0 to 2.5
0
Silver (Ag), % 0
0 to 0.1
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
44.5 to 45.5
Zinc (Zn), % 0
0 to 0.0010