EN 1.4826 Stainless Steel vs. Solder Alloy 716

EN 1.4826 stainless steel belongs to the iron alloys classification, while solder alloy 716 belongs to the otherwise unclassified metals. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.4826 stainless steel and the bottom bar is solder alloy 716.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
13
Elastic (Young's, Tensile) Modulus, GPa 200
51
Elongation at Break, % 9.1
13
Poisson's Ratio 0.28
0.36
Shear Modulus, GPa 77
19
Tensile Strength: Ultimate (UTS), MPa 500
39

Thermal Properties

Latent Heat of Fusion, J/g 310
60
Melting Completion (Liquidus), °C 1400
230
Melting Onset (Solidus), °C 1360
220
Specific Heat Capacity, J/kg-K 490
220
Thermal Conductivity, W/m-K 14
60
Thermal Expansion, µm/m-K 16
22

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
13
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
16

Otherwise Unclassified Properties

Density, g/cm3 7.7
7.3
Embodied Carbon, kg CO2/kg material 3.3
16
Embodied Energy, MJ/kg 47
270

Common Calculations

Stiffness to Weight: Axial, points 14
3.8
Stiffness to Weight: Bending, points 25
17
Strength to Weight: Axial, points 18
1.5
Strength to Weight: Bending, points 18
3.5
Thermal Diffusivity, mm2/s 3.7
37
Thermal Shock Resistance, points 11
2.5

Alloy Composition

Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.1
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
0 to 0.0020
Carbon (C), % 0.3 to 0.5
0
Chromium (Cr), % 21 to 23
0
Copper (Cu), % 0
0.3 to 0.7
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 60.4 to 68.7
0 to 0.020
Lead (Pb), % 0
0 to 0.070
Manganese (Mn), % 0 to 2.0
0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 9.0 to 11
0 to 0.010
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 1.0 to 2.5
0
Silver (Ag), % 0
0.8 to 1.2
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
97.6 to 98.9
Zinc (Zn), % 0
0 to 0.0010