EN 1.4826 Stainless Steel vs. N08366 Stainless Steel

Both EN 1.4826 stainless steel and N08366 stainless steel are iron alloys. They have 79% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4826 stainless steel and the bottom bar is N08366 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
180
Elastic (Young's, Tensile) Modulus, GPa 200
210
Elongation at Break, % 9.1
34
Fatigue Strength, MPa 140
190
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
80
Tensile Strength: Ultimate (UTS), MPa 500
590
Tensile Strength: Yield (Proof), MPa 260
240

Thermal Properties

Latent Heat of Fusion, J/g 310
310
Maximum Temperature: Corrosion, °C 430
430
Maximum Temperature: Mechanical, °C 950
1100
Melting Completion (Liquidus), °C 1400
1460
Melting Onset (Solidus), °C 1360
1410
Specific Heat Capacity, J/kg-K 490
460
Thermal Conductivity, W/m-K 14
13
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
1.8
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.0

Otherwise Unclassified Properties

Base Metal Price, % relative 17
33
Density, g/cm3 7.7
8.1
Embodied Carbon, kg CO2/kg material 3.3
6.2
Embodied Energy, MJ/kg 47
84
Embodied Water, L/kg 160
200

Common Calculations

PREN (Pitting Resistance) 23
42
Resilience: Ultimate (Unit Rupture Work), MJ/m3 39
160
Resilience: Unit (Modulus of Resilience), kJ/m3 170
150
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 18
20
Strength to Weight: Bending, points 18
19
Thermal Diffusivity, mm2/s 3.7
3.4
Thermal Shock Resistance, points 11
13

Alloy Composition

Carbon (C), % 0.3 to 0.5
0 to 0.035
Chromium (Cr), % 21 to 23
20 to 22
Iron (Fe), % 60.4 to 68.7
42.4 to 50.5
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 0 to 0.5
6.0 to 7.0
Nickel (Ni), % 9.0 to 11
23.5 to 25.5
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 1.0 to 2.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030