EN 1.4826 Stainless Steel vs. ZA-12

EN 1.4826 stainless steel belongs to the iron alloys classification, while ZA-12 belongs to the zinc alloys. There are 30 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.4826 stainless steel and the bottom bar is ZA-12.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
89 to 100
Elastic (Young's, Tensile) Modulus, GPa 200
83
Elongation at Break, % 9.1
1.6 to 5.3
Fatigue Strength, MPa 140
73 to 120
Poisson's Ratio 0.28
0.26
Shear Modulus, GPa 77
33
Tensile Strength: Ultimate (UTS), MPa 500
260 to 400
Tensile Strength: Yield (Proof), MPa 260
210 to 320

Thermal Properties

Latent Heat of Fusion, J/g 310
120
Maximum Temperature: Mechanical, °C 950
100
Melting Completion (Liquidus), °C 1400
430
Melting Onset (Solidus), °C 1360
380
Specific Heat Capacity, J/kg-K 490
450
Thermal Conductivity, W/m-K 14
120
Thermal Expansion, µm/m-K 16
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
28
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
42

Otherwise Unclassified Properties

Base Metal Price, % relative 17
11
Density, g/cm3 7.7
6.0
Embodied Carbon, kg CO2/kg material 3.3
3.4
Embodied Energy, MJ/kg 47
64
Embodied Water, L/kg 160
440

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 39
4.0 to 20
Resilience: Unit (Modulus of Resilience), kJ/m3 170
260 to 620
Stiffness to Weight: Axial, points 14
7.6
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 18
12 to 19
Strength to Weight: Bending, points 18
15 to 20
Thermal Diffusivity, mm2/s 3.7
43
Thermal Shock Resistance, points 11
9.4 to 14

Alloy Composition

Aluminum (Al), % 0
10.5 to 11.5
Cadmium (Cd), % 0
0 to 0.0060
Carbon (C), % 0.3 to 0.5
0
Chromium (Cr), % 21 to 23
0
Copper (Cu), % 0
0.5 to 1.2
Iron (Fe), % 60.4 to 68.7
0 to 0.075
Lead (Pb), % 0
0 to 0.0060
Magnesium (Mg), % 0
0.015 to 0.030
Manganese (Mn), % 0 to 2.0
0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 9.0 to 11
0 to 0.020
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 1.0 to 2.5
0 to 0.060
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
0 to 0.0030
Zinc (Zn), % 0
87.1 to 89