EN 1.4835 Stainless Steel vs. Commercially Pure Zinc

EN 1.4835 stainless steel belongs to the iron alloys classification, while commercially pure zinc belongs to the zinc alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4835 stainless steel and the bottom bar is commercially pure zinc.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
87
Elongation at Break, % 43
38
Poisson's Ratio 0.28
0.25
Shear Modulus, GPa 77
35
Tensile Strength: Ultimate (UTS), MPa 750
97
Tensile Strength: Yield (Proof), MPa 350
79

Thermal Properties

Latent Heat of Fusion, J/g 320
110
Maximum Temperature: Mechanical, °C 1150
90
Melting Completion (Liquidus), °C 1400
410
Melting Onset (Solidus), °C 1360
400
Specific Heat Capacity, J/kg-K 490
390
Thermal Conductivity, W/m-K 15
110
Thermal Expansion, µm/m-K 17
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
27
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
37

Otherwise Unclassified Properties

Base Metal Price, % relative 17
11
Density, g/cm3 7.7
6.6
Embodied Carbon, kg CO2/kg material 3.3
2.8
Embodied Energy, MJ/kg 47
53
Embodied Water, L/kg 160
340

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 270
34
Resilience: Unit (Modulus of Resilience), kJ/m3 310
36
Stiffness to Weight: Axial, points 14
7.4
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 27
4.1
Strength to Weight: Bending, points 24
7.1
Thermal Diffusivity, mm2/s 4.0
44
Thermal Shock Resistance, points 16
3.0

Alloy Composition

Aluminum (Al), % 0
0 to 0.010
Cadmium (Cd), % 0
0 to 0.010
Carbon (C), % 0.050 to 0.12
0
Cerium (Ce), % 0.030 to 0.080
0
Chromium (Cr), % 20 to 22
0
Copper (Cu), % 0
0 to 0.080
Iron (Fe), % 62 to 68.4
0 to 0.020
Lead (Pb), % 0
0 to 0.030
Manganese (Mn), % 0 to 1.0
0
Nickel (Ni), % 10 to 12
0
Nitrogen (N), % 0.12 to 0.2
0
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 1.4 to 2.5
0
Sulfur (S), % 0 to 0.015
0
Tin (Sn), % 0
0 to 0.0030
Titanium (Ti), % 0
0 to 0.020
Zinc (Zn), % 0
99.827 to 100