EN 1.4841 Stainless Steel vs. ASTM A182 Grade F10

Both EN 1.4841 stainless steel and ASTM A182 grade F10 are iron alloys. They have 82% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4841 stainless steel and the bottom bar is ASTM A182 grade F10.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
190
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 32
34
Fatigue Strength, MPa 200
180
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
74
Shear Strength, MPa 430
420
Tensile Strength: Ultimate (UTS), MPa 650
630
Tensile Strength: Yield (Proof), MPa 260
230

Thermal Properties

Latent Heat of Fusion, J/g 330
290
Maximum Temperature: Mechanical, °C 1150
600
Melting Completion (Liquidus), °C 1380
1420
Melting Onset (Solidus), °C 1340
1370
Specific Heat Capacity, J/kg-K 490
470
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.9
15
Electrical Conductivity: Equal Weight (Specific), % IACS 2.2
17

Otherwise Unclassified Properties

Base Metal Price, % relative 25
18
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 4.3
3.6
Embodied Energy, MJ/kg 62
51
Embodied Water, L/kg 190
120

Common Calculations

PREN (Pitting Resistance) 26
8.0
Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
170
Resilience: Unit (Modulus of Resilience), kJ/m3 170
140
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 23
22
Strength to Weight: Bending, points 21
21
Thermal Shock Resistance, points 15
18

Alloy Composition

Carbon (C), % 0 to 0.2
0.1 to 0.2
Chromium (Cr), % 24 to 26
7.0 to 9.0
Iron (Fe), % 47.1 to 55.5
66.5 to 72.4
Manganese (Mn), % 0 to 2.0
0.5 to 0.8
Nickel (Ni), % 19 to 22
19 to 22
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 1.5 to 2.5
1.0 to 1.4
Sulfur (S), % 0 to 0.015
0 to 0.030